MIL SPEC PRIMERS

WASH PRIMER


Wash Primer
DOD-P-15328 Zinc Chromate Yellow / Acid Etch
2 Component, 2 Gal Kit, 1 to 1 Mix Ratio, Air Dry Cure (<30 min)
Applied to clean metal surfaces of all types prior to application of coating system. Not intended to be a protective coating in itself.
Thickness: .00076 to .00127 cm
VY-113-3 Yellow Wash Primer


Wash Primer
Non  Chromate Black / Acid Etch
2 Component, 2 Gal Kit, 1 to 1 Mix Ratio, Air Dry Cure (<30 min)
Applied to clean metal surfaces of all types prior to application of coating system. Not intended to be a protective coating in itself.
Thickness: .00076 to .00127 cm
VY-116-3 Black Wash Primer


Wash Primer
Non  Chromate White / Acid Etch
2 Component, 2 Gal Kit, 1 to 1 Mix Ratio, Air Dry Cure (<30 min)
Applied to clean metal surfaces of all types prior to application of coating system. Not intended to be a protective coating in itself.
Thickness: .00076 to .00127 cm
VY-117-3 White Wash Primer

COATING COMPOUND


Coating Compound, Metal Pretreatment, Resin Acid
Mil-C-8514C Ty1 or Ty2 Zinc Chromate Yellow / Acid Etch
2 Component, 2 Gal Kit, 1 to 1 Mix Ratio, Air Dry Cure (<30 min)
Applied to clean metal surfaces of all types prior to application of coating system. Not intended to be a protective coating in itself.
Thickness: .00076 to .00127 cm
Mil-C-8514C Yellow Wash Primer

EPOXY POLYAMIDE PRIMER


Epoxy Polyamide Primer
MIL-PRF-23377, High Solids, Corrosion Inhibiting
Ty1 Class C Strontium Chromate Yellow, or Ty2 Class C Strontium Chromate 383 Green (Fed Std Color #34904)
2 Component, 1 Gal Kit, 3 to 1 Mix Ratio, Air Dry Cure or Bake Cure
Applied to pretreated metal surfaces of all types prior to application of topcoat or used alone.
Chemical and Solvent Resistant
Thickness: 0.6 to 0.9 Mil


Epoxy Polyamide Primer
MIL-PRF-23377, High Solids, Corrosion Inhibiting
Ty1 Class N Non-Chromate White, or Ty2 Class N Non-Chromate 383 Green (Fed Std Color #34094)
2 Component, 1 Gal Kit, 3 to 1 Mix Ratio, Air Dry Cure or Bake Cure
Applied to pretreated metal surfaces of all types prior to application of topcoat or used alone.
Chemical and Solvent Resistant
Thickness: 0.6 to 0.9 Mil

EPOXY PRIMER


Epoxy Primer
MIL-P-53022, High Solids, Corrosion Inhibiting Lead Chromate Free
Ty1 or Ty2 Non-Chromate White
2 Component, 1 Gal Kit, 3 to 1 Mix Ratio, Air Dry Cure or Bake Cure
Applied to pretreated metal surfaces of all types prior to application of topcoat or used alone.
Chemical and Solvent Resistant
Thickness: 0.6 to 0.9 Mil

ALKYD PRIMER


Alkyd Primer
TT-P-1757, High Solids, Corrosion Inhibiting Lead Chromate Free
Ty1 Zinc Chromate or Ty2 Non-Chromate 
Single Component, 1 Gal Air Dry Cure or Bake Cure
Applied to pretreated metal surfaces of all types prior to application of topcoat or used alone.
Chemical and Solvent Resistant
Thickness: 0.6 to 0.9 Mil